Jade white EVA film

Introduction:

With a stable inner structure , it is suitable for both indoor and outdoor lamination . It is a magic and basic material . By using one layer or stacking more layer , glass will perform a different color and light transmittance . Different kind of material like , fabric , PET and others could used together to create a unique project .

Specification:

Contact us
1.Introduction 

Jade white EVA film is also called acid white EVA film . It is with a very gentle luster like jade , which will make the glass projects look very upscale.  Different from color EVA film from other suppliers , this kind of jade white eva film could be used for outdoor projects, as it is thermoset material .


2.Specification

Thickness(mm) 0.38 0.76
width(m) 2/2.1/ 2.2/ 2.3 / 2.4 2/2.1/ 2.2/ 2.3 / 2.4
Length (m) 50 50


3.Performance data

Gel content >85%
Transmittance 83.2%
UV filtering rate 99%
Adhesion with glass 95 N /cm
shadow blocking rate 81%
Elongation 500%
Water absorption < 0.1%


4.Weather resistance test

Test Test Conditions Test Results
Boiling test 2 hour in 100 ℃ water No water penetration , no bubble ,no de- lamination and no haze appearance
Heat and humidity testⅠ Temperature 60℃, humidity 97%, 400 hours No water penetration , no bubble ,no de - lamination and no haze appearance
Heat and humidity test Ⅱ Temperature 85℃, humidity 85%, 1000 hours Haze appeared at 3.5 cm from the edge with no bubbles and de- lamination


5.Packing 

Packing PE plastic roll core + tinfoil vacuum bag+ leatheroid + water proof kraft paper
label There are product labels on both ends of each roll to indicate the production date, specifications and other information
Others If there are special packaging requirements, the packaging can be negotiated in advance


6. Processing method 

 First section :     60℃   20min
 Second section :  120℃   45min